Abstract
The corrosion behaviour of four nickel free austenitic stainless steels were investigated in 0·5M H2SO4 and 0·5M H2SO4 plus 0·4M NaCl solutions by means of potentiodynamic and potentiostatic anodic polarisation testing. The performances of the nickel free alloys are compared to those of an experimental intermediate nickel alloy (4%Ni) and a standard AISI 304 steel grade. Once passivity was reached all alloys displayed similar current densities ip in 0·5M H2SO4, independent from alloying. Mo and Cu were shown to be beneficial in decreasing the active dissolution currents and icrit values. The commercial AISI 304 steel displayed superior resistance to pit initiation during potentiodynamic testing, and AISI 304 steel displayed the highest Epit value of all alloys tested. When tested potentiostatically the N and Mo alloyed nickel free alloys showed excellent resistance to pit initiation and growth. The dominant effect of N was associated with repassivation of incipient pits, while Mo appeared to act at an earlier stage, suppressing initiation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.