Abstract
The inhibitive power of Polyvinyl Alcohol (PVA) was investigated toward the corrosion of carbon steel in 0.2N H2SO4 solution in the temperature range of 30-60˚C and PVA concentration range of 150-2000 ppm.
 The corrosion rate was measured using both the weight loss and the electrochemical techniques. The weight loss results showed that PVA could serve as a corrosion inhibitor but its inhibition power was found to be low for the corrosion of carbon steel in the acidic media. Electrochemical analysis of the corrosion process of carbon steel in an electrochemical corrosion cell was investigated using 3-Electrode corrosion cell. Polarization technique was used for carbon steel corrosion in 0.2N H2SO4 solutions in presence and absence of the inhibitor investigated. Electrochemical runs were done in the PVA concentrations of 150, 1000, and 2000 ppm and temperatures of 30, 40, 50, and 60˚C.
 It was shown that the inhibition efficiency for PVA decreased with increasing temperature at a given PVA concentration. On the other hand it was shown that at given temperature the inhibition efficiency of PVA was increased with increasing of PVA concentration in the corrosive acid until a PVA concentration of 2000 ppm was reached.
 The Maximum inhibition efficiency reached was about 71 % at 30ºC and 2000 ppm concentration, calculated by the weight loss technique. It was indicated also that the corrosion of carbon steel in 0.2N H2SO4 is highly activation controlled and inhibition action is occurring at both anodic and cathodic sites on the metal surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Iraqi Journal of Chemical and Petroleum Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.