Abstract

A series of binary Ti-Cu alloys containing 5-20 mass% Cu was prepared, and the corrosion behavior of alpha-Ti and Ti2Cu composing the Ti-Cu alloys were examined based on the anodic polarization curves and released ions in 0.9% NaCl and 1% lactic acid solutions. In both solutions, the Ti-Cu alloys showed the same anodic polarization curves as titanium in the condition below 1.4 V. However, precipitation of Ti2Cu contributed to a small increase in current densitiy in the transpassive region beyond 1.4 V. The amount of Cu ions released from Ti2Cu was 0.260 and 1.003 (microg/cm2/7 days) in 0.9% NaCl and 1% lactic acid solutions respectively. Although these values were larger than those from alpha-Ti (0.0379 +/- 0.0041 and 0.0962 +/- 0.0327 (microg/cm2/7days) in NaCl and lactic acid solutions respectively), they were not greater than those from type 4 gold alloy under the same conditions.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.