Corrosion Behavior of Plasma Nitrided SS316L Biomaterial
Highlights
MethodsThe plasma nitriding process on the surface of SS316L was performed at 350oC, 400oC, 450oC, 500oC, 550oC and 1.8 mbar nitrogen gas pressure for 3 hours
Biomaterials are materials that have already been used in medical devices or been in contact with biological system and they do not negatively affect the living organism and its components [1]
This research aims to determine the effect of plasma nitriding process to corrosion behavior of biomaterial SS316L
Summary
The plasma nitriding process on the surface of SS316L was performed at 350oC, 400oC, 450oC, 500oC, 550oC and 1.8 mbar nitrogen gas pressure for 3 hours. The corrosion resistance was investigated using three-electrode cell polarization method