Abstract
This research aimed to conduct a passive layer state study on martensitic and semi-austenitic precipitation hardening stainless steels (PHSS) passivated in citric acid and nitric acid baths at 49 and 70 °C for 50 and 75 min and subsequently exposed in 5 wt.% NaCl and 1 wt.% H2SO4 solutions. Corrosion behavior of the passivated material was observed by using potentiodynamic polarization (PP) according to the ASTM G5-11 standard. The microstructural analysis was performed by optical microscopy and scanning electron microscopy (SEM), while the passivated layer was characterized by X-ray photoelectron spectroscopy (XPS). The results indicated that the semi-austenitic-NA-50 min-70 °C sample showed the best corrosion resistance behavior in both solutions. The XPS characterization confirmed that the martensitic and semi-austenitic surface film presented a mixture of chemical compounds, such as Cr2O3 and Fe(OH)O, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.