Abstract
This paper presents the results obtained and the discussions made from a series of corrosion experiments involving Nickel alloy (ASTM A 494 M) reinforced with fused SiO2, size of the particles dispersed varies from 80-120 µm and amount of addition varies from 3 to 12 wt.% in steps of 3 wt.%. The resulting chilled MMCs are solidified under the influence of copper chill of 25 mm thickness to study the effect of corrosion behavior. Corrosion resistance was found to increase significantly with increase in SiO2 content in chilled MMCs. Nevertheless, even with high SiO2 content corrosion attack ie., pitting was found to be most severe during the initial stages of each test but it invariably decreased to a very low value in the later stages, due to the formation of an adherent protective layer on the MMCs developed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.