Abstract
AbstractThe corrosion properties of γ′-strengthened Co-xNi-Al-W-Cr (where x=15, 20, 25, and 30 at.%) superalloys were investigated in the mixture of 75 wt.% Na2SO4+25 wt.% NaCl at 900°C. The results showed that the corrosion behavior is associated with both sulfuration and oxidation processes. It was demonstrated that increasing the addition of Ni effectively promoted the formation of continuous Al2O3 scales, so that the hot corrosion resistance could be improved. When Ni content is more than 20 at.%, a large amount of Ni3S2 precipitates during the corrosion process. Sulfuration can destroy the integrity of the corrosion layer and increase the activity of oxygen. In this way, the internal oxidation of the alloys becomes more serious. Therefore, it is recommended that the optimum Ni addition is about 20 at.% for new type Co-Ni-Al-W-Cr superalloys.