Abstract
The dielectric, ferroelectric and piezoelectric properties of the high-Curie temperature (high-TC) 0.15Pb(Mg1/3Nb2/3)O3-0.38PbHfO3-0.47PbTiO3 (0.15PMN-0.38PH-0.47PT) ceramics synthesized by three different methods were investigated. The 0.15PMN-0.38PH-0.47PT ceramics prepared by the partial oxalate route present the best electrical properties (TC = 291 °C, εm = 28,937, Pr = 32.89 μC/cm2, Ec = 9.35 kV/cm, d33 = 456.2 pC/N and Kp = 67.2%) and excellent thermal stability of the piezoactivity properties under TC. Piezoresponse force microscopy (PFM) and confocal Raman microscopy (CRM) were employed to probe the nanoscale mechanism responsible for the performance difference of the 0.15PMN-0.38PH-0.47PT ceramics prepared by three different methods, disclosing the existence of the fine stripe domains, which make up the big island domains. The interplay between the macroscopic properties and nanoscopic domain structures of the 0.15PMN-0.38PH-0.47PT ceramics has been revealed. The better ferroelectric and piezoelectric response arise from the smaller domain size, which reduces the domain wall energy; whereas the higher coercive field Ec detected by the polarization-electric field (P-E) loops results from the harder domain switching for the 0.15PMN-0.38PH-0.47PT ceramics prepared by the wet chemical synthesis techniques.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.