Abstract
AbstractAdmittance spectroscopy measurement has been performed on NiOx thin films with various oxygen compositions (x=1.0-1.2) in order to characterize localized defect levels. The activation energy and concentration of localized defect levels in NiOx films with low oxygen composition (x≤1.07) are 120-170 meV and lower than 2×1019 cm-3, respectively. From I-V measurement of the Pt/NiOx/Pt structures, samples with high oxygen composition (x≥1.10) did not show resistance switching operation, while samples with low oxygen composition (x≤1.07) did. The best oxygen composition of NiOx thin films turned out to be 1.07 in order to realize repeatable and stable resistance switching operation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.