Abstract
Melting of native tapioca starch granules in aqueous pastes upon heating is observed in situ using simultaneous small- and wide-angle X-ray scattering (SAXS/WAXS) and solution viscometry. Correlated structure and viscosity changes suggest closely associated amylose and amylopectin chains in the semicrystalline layers, and the release of amylose chains for enhanced solution viscosity occurs largely after melting of the semicrystalline structure. Before melting, WAXS results reveal mixed crystals of A- and B-types (∼4:1 by weight), whereas SAXS results indicate that the semicrystalline layers are composed of lamellar blocklets of ca 43 nm domain size, with polydisperse crystalline (≃7.5 nm) and amorphous (≃1.1 nm) layers alternatively assembled into a lamellar spacing of ≃8.6 nm with 20% polydispersity. Upon melting, the semicrystalline lamellae disintegrate into disperse and molten amylopectin nanoclusters with dissolved and partially untangled amylose chains in the aqueous matrix which leads to increased solution viscosity. During subsequent cooling, gelation starts at around 347 K; successively increased solution viscosity coincides with the development of nanocluster aggregation to a fractal dimension ≃2.3 at 303 K, signifying increasing intercluster association through collapsed amylose chains owing to decreased solvency of the aqueous medium with decreasing temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.