Abstract
After high-temperature neutron irradiation of 1.4970 type steel M 23C 6 precipitation was observed in the matrix. This precipitate phase was found only at grain boundaries after thermal treatments. A unique feature of this irradiation-modified phase formation was that the M 23C 6 precipitates nucleated at the surfaces of pre-existing MC type carbides and grew in a very unusual way by forming facetted enclosures around the primary precipitates.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.