Abstract
Copper ferrite thin films, synthesized on clean stainless steel substrates from an alkaline non-aqueous solution at room temperature as a soft ferrite, were integrated into magnetic properties. Effect of annealing at 773 K for 1 h on structural, surface morphological and dielectric properties was reported. The tetragonal crystal structure and monodispersed non-uniformly distributed porous islands were confirmed from XRD and SEM analyses, respectively. The annealed copper ferrite thin film when used in magnetic studies showed saturation magnetization of 284 emu/cm 3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.