Conversion of preferred crystalline orientation by annealing and its impacts on the structural, electronic, and optical properties of pulsed laser-deposited CdO thin films

Abstract

The impact of annealing on the preferred crystalline orientation as well as the structural, electronic, and optical properties of pulsed laser-deposited 150 ± 3 nm thick cadmium oxide (CdO) films was studied. X-ray diffraction analysis revealed that the annealed CdO films have smaller crystallite sizes, as their molecules at the grain boundaries possessed enough kinetic energy to rearrange their preferred crystalline orientation between (111) and (200). The atomic force microscopy and field emission scanning electron microscopy analyses revealed an enhancement in the active surface area with optimized grain boundaries by annealing which facilitates gas adsorption/desorption. DC electrical conductivity depends on the annealing process and reveals two different conduction mechanisms. The direct optical energy gap was decreased from 3.41 eV to 2.76 eV by annealing at 473 K which is greater than the theoretical value, i.e. 2.2 eV, for bulk CdO. The findings agree with the Burstein-Moss effect as a result of the increased carrier concentration following the generation of numerous oxygen vacancy sites and Cd interstitials. However, mutual charge carrier-impurity interaction and charge carrier Columb interaction contributed to narrowing the band gap by increasing the annealing temperature. The enhanced values of Urbach energy, optical packing density, dispersion parameters, optical conductivity, dissipation factor, oscillator strength, and lattice dielectric constant supported the effectiveness of the annealing process on tailoring optoelectronic responses in the infrared region for the CdO thin films for use in optoelectronic devices. Moreover, the calculated linear optical susceptibility, and nonlinear constants (i.e. third-order optical susceptibility and nonlinear refractive index) were the highest for CdO films annealed at 473 K. The improved value of the figure of merit, solar material protection factor, and solar skin protection factor for the CdO films, annealed at 473 K supports its use in several photovoltaic applications, including solar cells.