Abstract
This manuscript presents the preparation of well-oriented @MgAl-layered double hydroxides (LDHs). It extends the reported preparation of SiO2@MgAl-LDH core-shell material (Si/(Si + Mg + Al) molar ratio = 0.54, Mg/Al = 2). There is introduced a new method for the gradual and controlled removal of the SiO2 core from SiO2@MgAl-LDH on treatment with a NaOH solution (1 M) for 1, 2, 4, and 6 h Si/(Si + Mg + Al) molar ratio from 0.06 to 0.52, Mg/Al = 2). Subsequent SiO2 leaching led to empty spheres with properties of the crystalline MgAl-LDH phase preserved. It is proved that @MgAl-LDH spheres formed do not collapse and hence, preserve their original spherical shape and structural properties. The potential of @MgAl-mixed oxides (MOs) obtained by thermal treatment of @MgAl-LDHs in catalysis is also demonstrated. When this material was used for the aldol condensation reaction of furfural with acetone, the best furfural conversion was obtained for @MgAl-MO with a Si/(Si + Mg + Al) molar ratio of 0.11.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.