AbstractIn this study, polyvinyl alcohol (PVA), gelatin (GEL) and gentamicin (GEN) were used and 13PVA/0.5GEL/GEN nanofibers were fabricated with the electrospinning method. These nanofibers were crosslinked chemically with glutaraldehyde (GA) at different time intervals (2, 3, 4, 5, 5.5 and 6 h) to observe the crosslinking effect on the properties of the nanofibers. Morphological analysis reported that as the crosslinking time increased, the nanofiber diameters also increased from 369.26 nm (non‐crosslinked) to 447.72 nm (6 h/crosslinking), respectively. The thermal characterization results demonstrated that crosslinking with different times noticeably shifted the thermal points.The tensile testing results proved that application of crosslinking enhanced the mechanical strength of the nanofibers from 3.31 MPa (non‐crosslinked) to 5.8 MPa (5.5 h/crosslinking), respectively. The GEN release profiles from the nanofibers showed similar behaviors under crosslinking and indicated that the crosslinking time did not have a significant effect on the amount of the GEN released.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.