Abstract
High-power impulse magnetron sputtering (HiPIMS) of materials systems with metal/gas-atom mass ratios mMe/mg near, or less than, unity presents a challenge for precise timing of synchronous substrate-bias pulses to select metal-ion irradiation of the film and, thus, reduce stress while increasing layer density during low-temperature growth. The problem stems from high gas-ion fluxes Fg+(t) at the substrate, which overlap with metal-ion fluxes FMe+(t). We use energy- and time-dependent mass spectrometry to analyze FMe+(t) and Fg+(t) for Group IVb transition-metal targets in Ar and show that the time-and energy-integrated metal/gas ion ratio NMe+/NAr+ at the substrate can be controlled over a wide range by adjusting the HiPIMS pulse length τON, while maintaining the peak target current density JT,peak constant. The effect is a consequence of severe gas rarefaction which scales with JT(t). For Ti-HiPIMS, terminating the discharge at the maximum JT(t), corresponding to τON=30μs, there is an essentially complete loss of Ar+ ion intensity, yielding NTi+/NAr+ ~60. With increasing τON, JT(t) decreases and NTi+/NAr+ gradually decays, due to Ar refill, to ~1 with τON=120μs. Time-resolved ion-energy distribution functions confirm that the degree of rarefaction depends on τON: for shorter pulses, τON<60μs, the original sputtered-atom Sigmund-Thompson energy distributions are preserved long after the HiPIMS pulse, which is in distinct contrast to longer pulses, τON≥60μs, for which the energy distributions collapse into narrow thermalized peaks. Thus, optimizing the HiPIMS pulse width minimizes the gas-ion flux to the substrate independent of mMe/mg.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have