Abstract
Abstract The transformation behavior of Ni50.5Mn30.4Ga19.1 and Ni53.7Mn26.4Ga19.9 was studied with ac magnetic susceptibility, differential scanning calorimetry, in-situ optical microscopy and X-ray diffractometry. The liquidus, solidus and L1 ŕ B2' temperatures were detected for the alloys. The transformation enthalpies of melting, solidification and martensitic/reverse reactions were determined. In Ni53.7Mn26.4Ga19.9 the magnetic transition was clearly below the parent to martensite phase transformation and did not have hysteresis. The transformation sequence is suggested as Pparam ŕ Tparam ŕ Tferrom with reverse reactions in respective order. In Ni50.5Mn30.4Ga19.1 the temperatures of the magnetic transition and structural phase transformations are close to each other and the Curie temperature shows a hysteresis of 9 K during cooling-heating cycle. Based on the combined measurements, the transformation sequences are assumed to be during cooling Pparam ŕ 7Mparam ŕ 7Mferrom ŕ Tferrom and Tferrom ŕ Tparam ...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call