Abstract
Objective: This study was done to evaluate shear bond strength (SBS) and modes of failures after different surface treatment modalities on polyetheretherketone (PEEK) implant abutments. Materials and methods: Seventy-five PEEK implant abutment specimens were randomly distributed into five groups based on surface treatment methods: Group I: No treatment, Group II: methylene blue-mediated photodynamic therapy (MB-PDT), Group III: neodymium-doped yttrium aluminum garnet (Nd:YAG) laser, Group IV: Sulfuric acid (H2SO4), and Group V: Sandblasting (Sb). The measurements for SBS and failure modes for PEEK implant abutment specimens were evaluated via Universal Testing Machine and Stereomicroscope, respectively. Two-way analysis of variance and Tukey's post-hoc test (p > 0.05) were used for the statistical analysis. Moreover, the Shapiro-Wilk normality test was also performed for normality. Results: The SBS mean values and standard deviations in megapascals (MPa) for PEEK abutment specimens with different surface pretreatment groups are shown in Table 1 and Fig. 1. The control group had the lowest SBS (9.67 ± 2.1 MPa), while the highest SBS was observed in Group II (MB-PDT; 17.21 ± 1.32 MPa). SBS values for Group IV (H2SO4; 15.83 ± 0.63 MPa) and Group III (Nd:YAG laser; 16.91 ± 2.10 MPa) were similar to Group II (MB-PDT; p > 0.05). The SBS values for the sandblasted specimens (13.90 ± 1.87 MPa) were not significantly different from the control group (p > 0.05). Conclusions: The PEEK implant abutment surfaces treated with MB-PDT and Nd:YAG laser expressed significantly improved SBS.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call