Abstract
The (Y,Yb)MnO3 thin films were prepared using alkoxy-derived precursor solutions. The hexagonal phase crystallized in Ar atmosphere and the films had high crystallinity and high degrees of c-axis orientation. The substitution of Y by Yb in YMnO3 lowered the crystallization temperature. The Y0.5Yb0.5MnO3 and YbMnO3 films crystallized at 700°C had c-axis orientation and showed the saturated P-E hysteresis loop. The remanent polarization and coercive field were 1.7 μC/cm2 and 100 kV/cm for Y0.5Yb0.5MnO3 film, and 2.1 μC/cm2 and 100 kV/cm for YbMnO3 film, respectively. The Y0.5Yb0.5MnO3 film crystallized at 700°C showed good fatigue property.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.