Abstract
The body-centered cubic (bcc) phase tends to preferentially nucleate during solidification of highly undercooled liquid droplets of binary alloy systems, including Fe–Co, Fe–Ni and Fe–Cr–Ni. We investigate a similar tendency during the partial devitrification of Co-rich amorphous precursors of composition (Co 1− x Fe x ) 88Zr 7B 4Cu 1 by identifying the structure and composition of the nanocrystalline grains. The Co:Fe ratio of the bcc nanocrystals varies linearly with the Co:Fe ratio of the amorphous precursor, and can lie well within the single-phase face-centered cubic (fcc) region of the Fe–Co phase diagram at the crystallization temperature. Classical nucleation theory therefore suggests several potential explanations for the preferential nucleation of bcc phase from an amorphous precursor, including: (i) a reduced amorphous/bcc interface energy as compared to the close-packed phases; (ii) a lower strain of precipitation for bcc nuclei as compared to close-packed fcc and hexagonal close-packed nuclei; and (iii) stabilization of the bcc phase by dissolved glass-formers such as Zr and B.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.