Comparison of different gettering techniques for Cu- p+ versus polysilicon and oxygen precipitates

Abstract

We performed measurements of gettering efficiencies for Cu in silicon wafers with competing gettering sites. Epitaxial wafers (p/p+) boron-doped with a polysilicon back side allowed us to compare p+ gettering with polysilicon gettering. We further measured metal distributions in p+/p- epitaxial test wafers, with the p- substrate wafers pretreated for oxygen precipitation to compare p+ gettering with oxygen precipitate gettering. Our test started with a reproducible spin-on contamination in the 1012 atoms/cm2 range, followed by thermal treatment in order to redistribute the metallic impurity. Wafers were then analyzed by a novel wet chemical layer-by-layer etching technique in combination with inductively coupled plasma mass spectrometry. This led to “stratigraphical” concentration profiles of the impurity, with typical detection limits of 5–10×1012 atoms/cm3. Twenty-five percent of the total Cu contamination in the p/p+/poly wafer was found in the p+ layer, whilst 75% was gettered by the polysilicon. Obviously, polysilicon exhibits a stronger gettering than p+ silicon, but due to the large distance from the front surface, polysilicon was less effective in reducing impurities from the front side of a wafer compared with p+ gettering. An epitaxial layer p+ on top of p- substrates with oxygen precipitates gettered 50% of the total Cu; while the other 50% of the Cu was measured in the p- substrate wafer with oxygen precipitates. Without oxygen precipitates, 100% of the spiked Cu contamination was detected inside the p+ layer. Gettering by oxygen precipitates thus occurs in the same temperature range as that where p+ silicon begins to getter Cu.