Comparison of cyclic fatigue resistance of four pediatric rotary file systems at body temperature: an in vitro study

Abstract

BackgroundThe aim of this study was to compare the cyclic fatigue resistance (CFR) of the newly developed pediatric nickel-titanium (NiTi) rotary file systems for root canal preparation of primary teeth.MethodsEighty pediatric NiTi rotary file systems files were used in this study, including 20 EasyInSmile X-Baby (25/0.04), 20 Scope miniScope (25/0.04), 20 EndoArt Pedo Gold (25/0.04), and 20 EndoArt Pedo Blue (25/0.04) files. Static CFR tests; performed on a custom-made stainless steel block with an inner diameter of 1.5 mm, an angle of curvature of 60° and a curved artificial canal with a radius of curvature of 5 mm. The test system was filled with distilled water and the temperature was kept constant at 35 ± 1 °C. The files were rotated in the simulated canal until fracture occurred. The number of cycles to failure (NCF) data was recorded, and all the fracture surfaces of the files were evaluated using scanning electron microscopy (SEM). One-way ANOVA and Tukey tests were used for statistical analysis of the data, and the significance level was set at p < 0.05.ResultsEndoArt Pedo Blue showed the highest NCF values (2668.10 ± 755.26), while the miniScope showed the lowest NCF values (453.65 ± 72.51), with a statistically significant difference between all the tested file systems (p < 0.05). There was no statistical difference in terms of fractured fragment lengths among all tested files (p > 0.05).ConclusionThe EndoArt Pedo Blue file system showed the best CFR performance among the four file systems specifically designed for primary teeth.