Abstract
Tetragonal zirconia polycrystals (TZP) can be used via CAD/CAM technique as metal replacement for fixed partial dentures. However, its intense white color and high opacity may represent an aesthetic limit. New TZPs with a claimed higher degree of translucency were recently marketed. The aim of the study was to investigate contrast ratio (CR), translucency parameter (TP), flexural strength (σ), Weibull characteristic strength (σ0 ), and Weibull modulus (m) of three "traditional" (IPS e.max Zir-CAD, inCoris ZI, VITA In-Ceram YZ) and two "increased translucency" (inCoris TZI, VITA In-Ceram YZ HT) Y-TZPs. For flexural strength, ISO 6872:2008 was followed. Bars (N = 40) were cut from pre-sintered blocks. Dense-sintering, finishing, and polishing were performed in order to obtain specimens of 15 × 4 × 1.2 mm. Samples were tested with three-point bending setup in a universal testing machine. For CR and TP, specimens (N = 10) were cut perpendicularly to the long axis from pre-sintered blocks. After the dense-sintering, specimens were finished and polished in order to obtain tiles of 12 × 15 × 1 mm. CR and TP were measured with a spectrophotometer equipped with an integrating sphere. No significant difference was found regarding flexural strength. A significant difference was found both for CR and TP among tested groups. VITA In-Ceram YZ HT and inCoris TZI showed the higher translucency. The difference was not statistically significant when compared with VITA In-Ceram YZ, and statistically significant when compared with IPS e.max Zir-CAD and inCoris ZI. The new "augmented translucency" TZPs showed higher translucency and similar flexural strength than "traditional" TZPs. Monolithic zirconia use is partially restricted due to the zirconia low translucency. The new "augmented translucency" zirconia showed a modest but perceptible increase in translucency and a similar flexural resistance, thus increasing the clinically suitable thickness range with optimized aesthetic and resistance. (J Esthet RestorDent 28:S32-S39, 2016).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.