Effects of Hydrothermal Treatment on the Phase Transformation, Surface Roughness, and Mechanical Properties of Monolithic Translucent Zirconia.

Abstract

This study aimed to investigate the effects of hydrothermal treatment on four types of monolithic, translucent, yttria-stabilized, tetragonal zirconia polycrystals (Y-TZPs). Two commercially available Y-TZP brands-SuperfectZir High Translucency (Aidite Technology Co, China) and Katana HT (Kuraray Noritake Dental, Japan) were assessed. For each brand of Y-TZP, materials of four coloring types, including noncolored (NC), colored by staining (CS), precolored (PC), and multilayered (ML) specimens were investigated after hydrothermal aging in an autoclave at 134°C/0.2 MPa for 0 (control group), 5, 10, and 20 hours. The tetragonal-to-monoclinic phase transformation, surface roughness, flexural strength, and structural reliability (Weibull analysis) were measured and statistically analyzed (α=0.05). The subsurface microstructure was analyzed with scanning electron microscopy. The group ML exhibited the lowest flexural strength and Weibull characteristic strength among the four coloring types (p<0.05). Slight increases in the monoclinic phase volume, flexural strength, and Weibull characteristic strength were observed after hydrothermal aging (pall<0.05). Regardless of coloring type, no significant effects of aging on the Weibull modulus or surface roughness were found for the tested materials. Compared with the Katana HT cross-sections, the SuperfectZir High Translucency cross-sections exhibited a similar but thicker transformation zone. The coloring procedure and material type were found to affect the mechanical properties and aging resistance of translucent monolithic Y-TZP ceramics. Regardless of the aging time, the surface roughness of the tested Y-TZP ceramics remained unchanged.