Abstract
Effect of auxiliary cathode (ACN) and conventional plasma nitriding (CPN) processes on surface modification of gamma-TiAl has been investigated. Both processes were done at temperature of 800 °C under gas ratio of N2/H2 = 1. The process duration was selected to be 3, 6 and 9 h for ACN, while it was 10, 20 and 30 h for CPN. Characterizations of the microstructure, phases, elemental distribution and hardness were performed using FESEM, XRD, GDOES, RBS and microhardness tests. Ti2AlN and TiN phases were detected as the main nitride compounds in both processes. Passive oxide films disrupted diffusion of nitrogen atoms in CPN process; hence a narrow nitrided zone was formed due to this surface oxidation. Higher ion intensity and oxidation protection emphasized the ACN process. The thicker and more uniform compound layers with more surface hardness were achieved using the auxiliary cathode. About 70% of nitriding process time was saved by ACN, in comparison with the CPN process.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call