Abstract
PurposePowder bed fusion-laser beam (PBF-LB) is a rapidly growing manufacturing technology for producing Al-Si alloys. This technology can be used to produce high-pressure die-casting (HPDC) prototypes. The purpose of this paper is to understand the similarities and differences in the microstructures and properties of PBF-LB and HPDC alloys.Design/methodology/approachPBF-LB AlSi10Mg and HPDC AlSi10Mn plates with different thicknesses were manufactured. Iso-thermal heat treatment was conducted on PBF-LB bending plates. A detailed meso-micro-nanostructure analysis was performed. Tensile, bending and microhardness tests were conducted on both alloys.FindingsThe PBF-LB skin was highly textured and softer than its core, opposite to what is observed in the HPDC alloy. Increasing sample thickness increased the bulk strength for the PBF-LB alloy, contrasting with the decrease for the HPDC alloy. In addition, the tolerance to fracture initiation during bending deformation is greater for the HPDC material, probably due to its stronger skin region.Practical implicationsThis knowledge is crucial to understand how geometry of parts may affect the properties of PBF-LB components. In particular, understanding the role of geometry is important when using PBF-LB as a HPDC prototype.Originality/valueThis is the first comprehensive meso-micro-nanostructure comparison of both PBF-LB and HPDC alloys from the millimetre to nanometre scale reported to date that also considers variations in the skin versus core microstructure and mechanical properties.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.