Abstract
We investigated the dependence of critical current density (Jc) on thickness of Yba2Cu3O7−δ (YBCO) films grown by pulsed laser deposition on (100) SrTiO3 (STO) and on rolling-assisted biaxially textured substrates (RABiTS). The thickness of YBCO films varied from 0.19 to 3 μm. The highest Jcs of 5.3 and 2.6 MA/cm2 at 77 K, self-field were obtained for 0.19-μm YBCO films on STO and RABiTS, respectively. Jc was found to decrease exponentially with YBCO thickness on both substrates. However, the results suggest different mechanisms are responsible for the Jc reduction in the two cases. On STO, growth of a-axis grains within c-axis films and broadening of the in-plane texture were observed in thick films. On RABiTS, degradation in cube texture as well as development of a porous surface morphology were found to correlate with film thickness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.