Abstract
Due to its unique material properties, such as extreme hardness and radiation resistance, silicon carbide has been used as an important construction material for environments with extreme conditions, like those present in nuclear reactors. As such, it is constantly exposed to energetic particles (e.g., neutrons) and consequently subjected to gradual crystal lattice degradation. In this article, the 6H-SiC crystal damage has been simulated by the implantation of 4 MeV C3+ ions in the (0001) axial direction of a single 6H-SiC crystal to the ion fluences of 1.359 1015 cm-2, 6.740 1015 cm-2, and 2.02 1016 cm-2. These implanted samples were subsequently analyzed by Rutherford and elastic backscattering spectrometry in the channeling orientation (RBS/C & EBS/C) by the usage of 1 MeV protons. Obtained spectra were analyzed by channeling simulation phenomenological computer code (CSIM) to obtain quantitative crystal damage depth profiles. The difference between the positions of damage profile maxima obtained by CSIM code and one simulated with stopping and range of ions in matter (SRIM), a Monte Carlo based computer code focused on ion implantation simulation in random crystal direction only, is about 10%. Therefore, due to small profile depth shifts, the usage of the iterative procedure for calculating crystal damage depth profiles is proposed. It was shown that profiles obtained by iterative procedure show very good agreement with the ones obtained with CSIM code. Additionally, with the introduction of channeling to random energy loss ratio the energy to depth profile scale conversion, the agreement with CSIM profiles becomes excellent.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.