Abstract

Objective: The objective of this study was to evaluate the effect of different surface treatment methods on the shear bond strength (SBS) of metal brackets bonded to two types of CAD/CAM composite restorations: milled and 3D-printed. Materials and Methods: A total of 160 flat-shaped specimens (10 × 10 × 2 mm3) were prepared from four different CAD/CAM composites; two milled (Lava Ultimate™ [LU] and Grandio™ [GR]) and two 3D-printed (Crowntec™ [CT] and C&B Permanent™ [CB]). These specimens underwent thermocycling (5000 cycles at 5–55 °C), then were categorized based on the surface treatment into four groups (n = 10): Group C (control, no surface treatment), Group HF (treated with 9.6% hydrofluoric acid), Group DB (mechanical roughening by a diamond bur), and Group SB (sandblasting using aluminum oxide). Metal brackets were bonded using Transbond XT Primer and universal adhesive, stored in artificial saliva for 24 h, then thermocycled again. Shear bond strength (SBS) was tested using a universal testing machine until bracket debonding occurred. The adhesive remnant index (ARI) was assessed using a stereomicroscope to quantify the residual adhesive following debonding. Result: Regarding material, GR and LU restorations had significantly higher SBS values compared to CT and CB, ranging from 13.90 MPa to 20.35 MPa. Regarding surface treatment, SB and HF groups showed significantly higher SBS values. The ARI scores showed different adhesive modes of failure, with higher instances of scores 0 and 1, which indicate no or minimal adhesive remaining. Conclusions: Both milled and 3D-printed materials had adequate SBS for clinical use, with milled materials showing superior results. Surface treatments like sandblasting and HF significantly improved bond strength, with adhesive failure being common.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.