Comparative analysis and antibacterial properties of thermally sintered apatites with varied processing conditions

Abstract

AbstractHydroxyapatite (HA) and biphasic hydroxyapatite/beta‐tricalcium phosphate (biphasic HA/β‐TCP) were synthesized using thermal sintering. The parameters‐ sintering temperature (600°C, 900°C, and 1200°C), biological source used (fish bone, egg shells, and fish scales), and soaking time (2, 6, and 10 hours) were permuted to study their effects on the properties of the resultant apatite. Morphological study revealed that the smallest (60 nm) spherical particle and the largest (470 nm) irregular shaped particle were obtained from the fish bone sample sintered at 600°C and at 1200°C respectively. FTIR and XRD results showed that as the sintering temperature is increased, the phase transformation from HA to β‐TCP takes place. Only the final products from fishbone sample at 600°C are pure carbonated HA. The crystallinity of synthesized particles ranged from 79% to 98%. Soaking time has no effect on phase composition of the apatite but has significant effect on crystallite size; increase in soaking time increases crystallite size and particle shape becomes more spherical. Interestingly, the fish bone sample sintered at 900°C has higher crystallinity and crystallite size compared to the fish scale sample sintered at the same temperature. EDX confirmed that non‐stoichiometric apatite with Ca/P ratio ranging from 1.47 to 1.91 can be obtained by varying the sintering conditions. The antibacterial test revealed that both calcium apatite obtained from fish bones and fish scales have inhibited bacterial growth; apatite from fish bone works faster than fish scales. The in vitro cytotoxicity test ensured that all the calcium apatite except for eggshell are non‐cytotoxic. Thus, apatite with excellent microbial activity can be obtained by using fish wastes, and by tuning the sintering parameters, the apatite with desired types and properties can be synthesized for different biomedical applications.