Abstract
Effects of CO adsorption on the magnetic properties of Fe films on Cu(001) were studied at 100 K as a function of the film thickness. CO adsorption does not affect the magnetic property of 2 ML Fe film but induces the spin reorientation transition from perpendicular to in-plane magnetization for 4 ML Fe film. It also causes the apparent decrease of magnetization, which is attributed to the reduction in surface magnetization by analyses of depth-resolved XMCD spectra. The reduction of the magnetization can be originated from a reconstruction of the surface structure of the films. It was suggested that the surface structures of the 4 ML Fe film are changed to a bcc-like structure upon CO adsorption, while the structure of the 2 ML Fe film could not change by CO adsorption because its magnetization is unchanged. [DOI: 10.1380/ejssnt.2008.233]
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.