Abstract
The corrosion resistance to calcium‑magnesium‑aluminum-silicate (CMAS) is a key property affecting the long-term durability of thermal barrier coatings (TBCs). Meanwhile, rare-earth hafnates are considered promising TBC candidates due to their low thermal conductivity and suitable thermal expansion coefficients. Thus, this study explores the CMAS corrosion resistance of Gd2(Hf0.7Ce0.3)2O7 (GH7C3) ceramic material under different conditions and compares it with the binary system Gd2Hf2O7 (GH) ceramic material. The findings indicate that GH7C3 can react chemically with CMAS and rapidly form a dense apatite crystalline layer at the interface between GH7C3 ceramic and CMAS, providing excellent CMAS resistance. Furthermore, the composition of the remaining CMAS melt Furthermore, the composition of the remaining CMAS melt undergoes compositional changes upon interaction, ultimately forming spinel in Mg and Al-enriched regions. In the meantime, CeO2 can promote the rapid formation of apatite crystals, significantly enhancing the CMAS resistance of GH7C3 to CMAS at high temperatures compared to GH.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.