Clinical and paraclinical control after traction screw and miniplate osteosynthesis of fractures of the mandibular condyle

Abstract

Particulate metal fragments have been identified histologically within the tissues adjacent to miniplates and screws after they have been removed. These were thought to have been caused by corrosion and degradation of the metal. However, the particles may have originated from rough edges or from protuberances left on the metal surface after cutting and machining during manufacture, and subsequently become detached. This study was undertaken to analyse the incidence and distribution of metal fragments on the surface of miniplates and screws before use. Fifteen miniplates and 60 screws were examined by stereomicroscopy and scanning electron microscopy. Rough metal edges or protuberances were identified on over half the samples, mostly in the countersink area of screw holes on the mini-plates. Fragments were detected within some of the cruciform screw heads and on some screw threads. We conclude that metal protuberances are present on the surface of mini-plate components when they are received from the manufacturer. There is a risk that the fragments might be detached and deposited into the tissues during insertion.