Abstract
In order to accomplish the circular cup drawing of the sheet material whose ductility is extremely poor under the cold forming condition, the Maslennikov's technique was applied. A deformable rubber ring was used instead of the hard punch. Test material was magnesium alloy AZ31-O sheet. Small die profile radius was applied, which was twice or 4 times of the sheet thickness. A semisolid lubricant was used for the lubrication of the blank - die interface, on the other hand, the rubber - blank interface was degreased to increase friction. The limiting drawing ratio of 1.31 was attained. A peculiar fracture mode arises, where the material suddenly fractured with crack evolution emanating from the flange periphery. The fracture strain is found approximately equal to the work hardening exponent n-value in plastic property. Another kind of crack arose in the circumferential direction of the cup during unbending process with smaller die profile radius. To decrease the scratched lines of the cup surface caused by very high sliding contact pressure to the die, high-speed drawing was tested using a drop-weight. The surface was improved, because the material - tool contact was successfully prevented by the hydrodynamic lubrication film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.