Abstract
Ba2NaNb5O15 (BNN) thin films with a tungsten bronze structure were fabricated using a precursor solution that was synthesized from barium, sodium, and niobium alkoxides. Highly (002)-oriented BNN films were prepared successfully on Pt(100)/MgO(100) substrates at 700°C, using a BNN underlayer. X-ray pole-figure measurement showed that the BNN films that crystallized on Pt(100)/MgO(100) substrates had two in-plane orientations. The remanent polarization and coercive field of the BNN film (thickness of 1.0 µm) that was crystallized at 700°C were 12.3 µC/cm2 and 101 kV/cm, respectively, at –150°C (123 K). BNN films on fused silica substrates exhibited second harmonic generation upon irradiation with 1064 nm light.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.