Abstract
The wood-based moldings were fabricated by using only citric acid as an adhesive. The mechanical properties, water resistances, thermal properties and chemical structure were investigated. Wood powder obtained from Acacia mangium was mixed with citric acid under certain weight ratios (0–40 wt%), and each powder mixture was molded using two types of metal molds at 200°C and 4 MPa for 10 min. The modulus of rupture and the modulus of elasticity values of the wood-based molding containing 20 wt% citric acid were 35.8 MPa and 5.4 GPa, respectively. The maximum impact strength was 0.94 kJ/m2 with the same citric acid content. The water resistance increased with increasing citric acid content, and the good resistance to boiling water was also recognized. However, some elution of substances derived from citric acid was observed at high levels of citric acid, causing a decrease in the thermal properties. The ester linkages were detected by Fourier transform infrared spectroscopy, indicating that the citric acid reacted with the wood. Our results demonstrated that citric acid brought about good adhesiveness for fabricating the wood-based molding.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.