Abstract

Ultrasonic welding is a well-known technique for joining thermoplastics and has recently been introduced for joining carbon fiber reinforced thermoplastic composites. However, there is a lack of understanding on how weld quality attributes develop under different welding conditions, especially without using an energy director. In this paper, ultrasonic welding of an injection molded short carbon fiber reinforced composite is tested to investigate three important weld attributes, bonding efficiency, weld area, and horn indentation. From a two-level full factorial experiment, welding energy is found having the most important influence on joint quality, which is related to weld attributes. Thus, only welding energy is varied to simplify the analysis of weld attributes evolution during the welding process. After examining the microstructure of the cross sections and the fracture surface of the welded joints, several observations were obtained. First, the bonding formation for the carbon fiber reinforced composite is mainly through the polymer–polymer interface healing with involved carbon fibers as reinforcements. Second, the bonding efficiency and weld area increase with an increase in welding energy until they reach a threshold. As welding energy continues to increase, the bonding efficiency will decrease due to material degradation as pores develop, but weld area will remain unchanged. Finally, the difference of welding attributes leads to three failure modes of the joints, e.g. interfacial separation, nugget shear fracture, and nugget pull-out fracture, which are an indicator of the joint quality. These experimental observations provide insights toward the development of a robust ultrasonic welding process for fiber reinforced composites.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.