Abstract
The hot deformation behavior of Ti-Al-Nb-Zr-Mo-Cr titanium alloy has been investigated using a Gleeble-1500D thermal simulation test machine in the temperature range of 855°C~1015°C,at constant strain rate from 0.01 s-1 to 10s-1 and with height reduction of 45%. The flow curves characteristic under different deformation parameters show significant difference. According to the stress-strain curves of the alloy and its stress characteristics, the Arrhenius constitutive equation was obtained. The average activation energy is about 541 kJ/mol in the α+β field, and about 243 kJ/mol in the β field, respectively. Based on the dynamic materials model, the processing map is generated, which shows that the peak efficiency domain appears at the temperature of 874°C~900°C and the strain rate of 0.001 s-1~0.06s-1 with a peak efficiency of 0.58 at about 887°C/0.001s-1.