Abstract
This study intends to investigate the early pozzolanic reaction of Nanosilica (nS) modified cement paste (NMCP) by the characterization technique of Calcium Hydroxide (CH) and Calcium Silicate Hydrate (C-S-H ) using Fourier Transform Infrared Spectroscopy (FT-IR). NMCP samples were prepared with water-binder ratio of 0.50. nS of 5-15nm particle size were used as 1%, 3% ,5% ,7% and 10% replacement of cement by weight. All samples were cured in the concrete laboratory at daily room temperature (T) and relative humidity (RH) in the range of 18-28oC and 65-90%, respectively. Powdered samples were prepared and tested at day 1,7,21 and 28. It was found that characterization technique used were able to give satisfactory qualitative indication of pozzolanic reactivity of NMCP by the presence and absence of C-S-H and C-H that can indicate which replacement has higher pozzolanicity. NMCP exhibited a higher pozzolanic reactivity compare to conventional cement paste by which cement performance was enhanced.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Civil Engineering, Science and Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.