Abstract
AbstractElectrically active defects in both 4H and 6H polytypes of SiC have been observed through the use of deep level transient spectroscopy (DLTS). Schottky contacts were grown by vapor phase epitaxy (VPE) with doping concentrations, the epitaxial layer having a doping concentration in the range of 1014 cm−3 to 1017cm−3. Numerous levels have been found in the as-grown n-type 6H-SiC samples and secondary ion mass spectrometry (SIMS) and MeV electron irradiation have been employed to corrrelate the defect levels to impurities or structural defects. In contrast, only a single level is observed in the as-grown 4H-SiC samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.