Abstract
Spherical mono-sized Sn-1.0Ag-0.5Cu (wt.%) particles with diameter ranging from 124.0 to 337.4μm were prepared by the pulsated orifice ejection method (termed “POEM”).These spherical Sn-1.0Ag-0.5Cu particles exhibit a good spherical shape and a narrow size distribution, suggesting that liquid Sn-1.0Ag-0.5Cu can completely break the balance between the surface tension and the liquid static pressure in the crucible micropores and accurately control the volume of the droplets. Furthermore, the relationship between cooling rate and microstructures of spherical Sn-1.0Ag-0.5Cu particles was studied with a specific focus on different particle diameter during the rapid solidification. The cooling rate of spherical Sn-1.0Ag-0.5Cu particles with different diameter was evaluated by the Newton’s cooling model. It is revealed that the cooling rate decreases gradually with the increase of particle size during the rapidly solidified process. When the particle diameter is equal to 75 μm, the cooling rate of the Sn-1.0Ag-0.5Cu particle achieves 4.30×103 K/s which indicates that smaller particles can rapidly solidified due to their higher cooling rate. Meanwhile, the cooling rate decreases rapidly when the particle diameter increases between 75 and 100 μm. Furthermore, the different particle diameter with different cooling rate has a great influence on the solidification microstructure of Sn-1.0Ag-0.5Cu particles. The cooling rate and grain boundary size decreases with the increase of particle diameter during the rapid solidification. In addition, the phase size of βSn increases with the decrease of particle size. Smaller particles have relatively high cooling rate and it gives less solidification time as compared to larger particles. It is an effective route for fabrication of high-quality spherical Sn-1.0Ag-0.5Cu particles. Keywords: Spherical Sn-1.0Ag-0.5Cu particles; Rapid solidification; Structural; Cooling rate
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.