Abstract
We investigated material and electrical properties of ZrO 2 films deposited by atomic layer deposition (ALD) using Zr t-butoxide and water (H 2 O). As-deposited ZrO 2 films show 2.4nm of CET measured at 100kHz with frequency dispersion and high leakage current (3A/cm2) at 1V. These undesirable properties may results from metallic Zr and carbon contamination in the films. The post-deposition annealing was performed in an O 2 ambient at 500 to improve the capacitance and reduce the leakage current. ZrO 2 films deposited by ALD and annealed at 500C exhibit CET(Capacitance Equivalent Thickness) of 2nm without dispersion issues and leakage current less than 10 m 3 A/cm 2 at 1V.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.