Abstract
High Speed Steel (HSS) tool is commonly used in engineering applications, especially as cutters. The shortfall of this materials are wear and corrosion. However, these can be reduced by coating the surface of the material. Therefore, the purpose of this research is to investigate the effects of Diamond Like Carbon (DLC) coating, quenching heating treatment, and tempering on the physical and mechanical properties of HSS surface. The physical characteristics which will be investigated is the micro structure, while the mechanical characteristics are hardness, wear and corrosion rate. HSS has variations in their chemical composition (% mass): 0.75–1.5 C, Co >12, V > 5, 4–4.5 Cr,10–20 W and Mo. Furthermore, DLC coating uses Plasma Assisted Chemical Vapor Deposition (PACVD) technique with variation in the duration of coating (1,2,3,4,5 and 6 hours) at temperature of 300℃, with pressure variations of 1.0, 1.2, 1.4, 1.6, 1.8 and 2.0 millibar. DLC coating material be treated from methane or ethane gas, which is streamed into the fire with Argon (Ar). The result shows variations in DLC coating and the hardness grade depends on the coating time and pressure variation. DLC coating for a duration of 4 hours under 1.8 mbar pressure can reduce the surface hardness of HSS tool by 62% accompanied by increased ductility.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.