Abstract
4H-SiC PiN rectifiers with implanted anode and single-zone JTE were fabricated using AlN capped anneal. The surface damage during the high temperature activation anneal is significantly reduced by using AlN capped anneal. The forward drop of the PiN rectifiers at 100A/cm2 is 3.0V while the leakage current is less than 10-7A/cm2 up to 90% breakdown voltage at room temperature. With 6μm thick and 2×1016cm-3 doped drift layer, the PiN rectifiers can achieve near ideal breakdown voltage up to 1050V. Hole impact ionization rate was extracted and compared with previously reported results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.