Abstract
ABSTRACT Water-granulated CaO-modified iron-silicate slags have shown beneficial properties for cement applications. To further evaluate potential applications, the leaching properties must be understood. Therefore, this study aims to characterise and assess the metal leaching of iron-silicate slags (2.6% CaO) modified with lime (CaO, up to 20 wt.%) produced on both laboratory and industrial scales. The granulated samples showed amorphous contents for the studied CaO range. Generally, the metal content of the samples decreased with the increasing CaO content. Batch leaching tests were conducted on the slags, and the metal leaching and CaO content of the slag were strongly correlated. The leaching of Zn and Cu decreased with the increasing CaO content in the slag. Overall, the slags with 12–13% CaO exhibited minimal leaching of Zn, Cu, Ni, and Sb. These findings indicate that CaO influences the properties of the slag and can suppress metal leaching from water-granulated iron-silicate slags.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call