Abstract
Molecular weight increase via chain extension reactions of poly(ethylene terephthalate) with commercially available diepoxides was studied in a custom-made laboratory scale reactor and a Brabender rheomixer under reactive blending conditions. The products were characterized by carboxylic end group analysis, intrinsic viscosity, and differential scanning calorimetry. PET was effectively modified in the laboratory-scale reactor using cyclic diepoxides because the resulting polymers show intrinsic viscosities that are comparable to virgin PET (0.68–0.75 dL/g vs. 0.74 dL/g) and much higher than processed PET (0.55), while carboxyl contents were reduced to a third of that of the virgin PET. Diglycidyl ethers produced polymers displaying decreased viscosity values, increased carboxyl content, and lower melting points. Low concentrations of extender and short reaction times generally favored chain extension. In addition, purging with nitrogen resulted in chain extended polymers having the highest values of intrinsic viscosity ([η] = 0.79, 0.82). Similar trends were observed with modified products in the rheomixer having somewhat smaller viscosity values, larger carboxyl contents, and increased melting points. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 2121–2127, 1999
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.