Abstract
The upcoming UCNProBe experiment at Los Alamos National Laboratory will measure the beta decay rate of free neutrons with different systematic uncertainties than previous beam-based neutron lifetime experiments. We have tested a new 10B-coated Yttrium Aluminum Perovskite (YAP:Ce) scintillator and present its properties. The advantages of the YAP:Ce scintillator include its high Fermi potential, which reduces the probability for upscattering of ultracold neutrons (UCN), and its short decay time, which increases sensitivity at high counting rates. Birks' coefficient of YAP:Ce was measured to be (5.56-0.30+0.05)×10-4 cm/MeV. The loss of light due to the 120nm 10B-coating was measured to be about 60%, and the loss of light from YAP:Ce due to transmission through a deuterated polystyrene scintillator was about 50%. The efficiency for neutron capture on the 10B coating was (86.8 ± 2.6)%, and a measurement using UCN showed that the YAP:Ce crystal counted 8%-28% more UCN compared to a ZnS:Ag screen. The difference may be due to the uneven coating of 10B on the rough surface of ZnS:Ag.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.