Abstract
The cathodoluminescent properties of nanocrystalline Lu3Ga5O12:Tb3+ phosphor films were investigated. Phosphor films were prepared on indium tin oxide coated glass by a screen printing method. The Lu3Ga5O12:Tb3+ phosphor is mixed with In2O3 nanoparticles to improve the luminescence and degradation properties of phosphor films under electron excitation. Cathodoluminescent spectra and luminance degradation behavior of the Lu3Ga5O12:Tb3+ phosphor films under electron bombardment were studied. Enhancement of the luminescence was observed after being mixed with In2O3 nanoparticles. Also, the In2O3 mixed Lu3Ga5O12:Tb3+ phosphor shows improvement of the resistance to the electron bombardment. The results show that the Lu3Ga5O12:Tb3+ phosphor is stable under electron bombardment and has potential for application in field emission display devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics: Materials, Processing, Measurement, and Phenomena
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.