Abstract
Zinc oxide (ZnO) ceramics was coupled and reacted with alpha aluminum oxide (α-Al2O3) ceramics at 1200oC for 24 h. SEM observation and energy dispersive X-ray spectroscopy (EDS) analysis revealed the existence of diffusion layer of 10 μm thickness on the α-Al2O3 side of interface between ZnO and α-Al2O3. The diffusion layer is considered to consist of a ZnAl2O4, from the result of XRD. The cathodoluminescence of the diffusion layer was compared with that of zinc aluminate (ZnAl2O4) ceramics synthesized by conventional solid state reaction method. The single phase ZnAl2O4 showed weak emission peaked at 4.6 eV. On the other hand, the diffusion layer showed intense emission peaked at 3.75 eV. The ZnAl2O4 on the α-Al2O3 side of the interface synthesized by coupling of ZnO and α-Al2O3 is considered to be a excellent material as an ultraviolet light emitter.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.