Catalytic performance and durability of Ni/AC for HI decomposition in sulfur–iodine thermochemical cycle for hydrogen production

Abstract

This work reports the Ni content effect on the Ni/AC catalytic performance in the HI decomposition reaction of the sulfur–iodine (SI) thermochemical cycle for hydrogen production and the Ni/AC catalyst durability in a long-term test. Accordingly, five catalysts with the Ni content ranging from 5% to 15% were prepared by an incipient-wetness impregnation method. The activity of all catalysts was examined under the temperature range of 573–773K. The catalytic performance evaluation suggests that Ni content plays a significant role in the Ni dispersion, Ni particle size, and eventually the catalytic activity in HI decomposition. 12% is the optimal Ni content for Ni/AC catalysts in HI decomposition which is balanced between poor dispersion of Ni particles and increasing active center. The results of 24h durability test, which incorporated with BET and TEM investigations of the 12%Ni/AC catalyst before and after the reaction, indicate that establishing a better Ni particle dispersion pattern and improving the stability of Ni particles on the support should be considered in the future.